Slim (expanded ID:36mm) and thin (wall thickness after recovered: 0.05mm)
Shrink ratios are either 2:1 or 4:1, covering wide range.
High flexibility, high tearing strength and high resistance to wear
Radiation sterilizable (gamma ray, electron beam)
Low longitudinal shrinkage(for tubes with 2:1 shrink ratio, -15%)
Superior surface finish and high adhesion to the target material
Note:
Longitudinal change is measured by Penn&Nitto and not provided by Cobalt Polymers.
Use this value only as a guide. For the tubes with the shrink ratio 4:1, the longitudinal change is large. It was -60% in our laboratory test.
If there is any specified filling material, we will measure the longitudinal change and the optimal shrinkage engineering using the material. Other tests including shrinkage properties and wall thicknesses before and after recovery can be provided selectively; however, we will be able to test only part of your samples.
Please note that these tests results are not guaranteed by Cobalt Polymers so use them as references.
Applications
Palladium™ Pebax® Heat Shrink Tubing Dimensions
Durometer (after recovery): 72° 2:1 shrink ratio Length: 1.2m
Contact us for tube lengths.
Product ID
Expanded ID (mm)
Recovered ID (mm)
Recovered Wall thickness (mm)
Color
Package unit
H-P2-014-002-CLR
0.36
0.17
0.050
Clear
20
H-P2-040-004-BLK
0.91
0.50
0.101
Black
H-P2-060-010-CLR
1.52
0.89
0.254
Clear
H-P2-060-003-CLR
1.52
0.89
0.076
Clear
H-P2-140-006-CLR
3.30
1.90
0.152
Clear
Durometer (after recovery):40° 2:1 Shrink ratio Length: 1.2m
Contact us for tube lengths.
Product ID
Expanded ID (mm)
Recovered ID (mm)
Recovered Wall thickness (mm)
Color
Package unit
H-P2-040-004-40-CLR
0.91
0.50
0.100
Clear
20
H-P2-060-003-40-CLR
1.50
0.89
0.075
Clear
H-P2-060-010-40-CLR
1.50
0.89
0.250
Clear
H-P2-140-006-40-CLR
3.30
1.90
0.150
Clear
Durometer (after recovery):72° 4:1 Shrink ratio Length: 0.3m